Effect of Cutting-Edge Geometry and Workpiece Hardness on Surface Residual Stresses in Finish Hard Turning of AlSl 52100 Steel  

Oleh:

Melkote, Shreyes N. ; Jeffrey D. Thiele, ; Watkins, Thomas R. ; Peascoe, Roberta A.

Jenis: Article from Journal - ilmiah internasional
Dalam koleksi: Journal of Manufacturing Science and Engineering vol. 122 no. 4 (Nov. 2000), page 642-649.
Topik: GEOMETRY; cutting - edge geometry; workpiece hardness; finish hard turning

Ketersediaan

Perpustakaan Pusat (Semanggi) Nomor Panggil: JJ93.2 Non-tandon: 1 (dapat dipinjam: 0) Tandon: tidak ada

Lihat Detail Induk

Isi artikel

An experimental investigation was conducted to determine the effects of tool cutting - edge geometry (edge preparation) and workpiece hardness on surface residual stresses for finish hard turning of through - hardened AISI 52100 steel. Polycrystalline cubic boron nitride (PCBN) inserts with representative types of edge geometry including "up - sharp" edges, edge hones, and chamfers were used as the cutting tools in this study. This study shows that tool edge geometry is highly influential with respect to surface residual stresses, which were measured using x - ray diffraction. In general, compressive surface residual stresses in the axial and circumferential directions were generated by large edge hone tools in longitudinal turning operations. Residual stresses in the axial and circumferential directions generated by large edge hone tools are typically more compressive than stresses produced by small edge hone tools. Microstructural analysis shows that thermally - induced phase transformation effects are present at all feeds and workpiece hardness values with the large edge hone tools, and only at high feeds and hardness values with the small edge hone tools. In general, continuous white layers on the workpiece surface correlate with compressive residual stresses, while over - tempered regions correlate with tensile or compressive residual stresses depending on the workpiece hardness.